Accumulation of local defects in the zone of forced elasticity before the front of a failure crack in polymers

This article is dedicated to accumulation of local defects in the zone of forced elasticity before the front of a failure crack in polymers. The mechanism of microcavity formation in the crack and the mechanism of the break-up of loose junctions in the support framework were described. The kinetic equation of the break-up of loose junctions in the support framework was obtained, and the junction break-up time was calculated.

fluctuation, crack front, microheterogeneity, junction break-up time, Rayleigh distribution.

1. Валишин А.А., Мищенко Д.В. Особенности квазихрупкого разрушения полимеров и композитов на их основе // Вестник МИТХТ. 2010. Т. 5. № 6. С. 99–104.

2. Регель В.Р., Слуцкер А.И., Томашевский Э.Е. Кинетическая природа прочности твердых тел. – М.: Наука, 1974. 560 с.

3. Валишин А.А., Карташов Э.М., Тишаева С.Д. Статистические характеристики теплового движения в полимерах // Ученые записки МИТХТ. 2002. № 5. С. 11–18.

4. Патрикеев Г.А. Макромолекулярная механика // Механика полимеров. 1971. № 2. С. 221–231.

5. Бартенев Г.М. Прочность и механизм разрушения полимеров.– М.: Химия, 1984. 280 с.

6. Журков С.Н., Куксенко В.С., Петров В.А. О прогнозировании разрушения горных пород // Известия АН СССР. Физика Земли. 1977. № 6. С. 1–18.

7. Половников Г.В., Трофимов В.В. Характер акустической эмиссии и долговечность хрупких композитных материалов при постоянной нагрузке // Механика композиционных материалов. 1981. № 3. С. 542–546.

8. Осокина Д.И., Мячкин В.И., Игамназаров Т.И., Смирнов Л.А. Изучение локального поля напряжений аналога очаговой зоны (результаты моделирования) // В кн.: Физические процессы в очаге землетрясений. – М.: Наука, 1980. С. 68–78.

9. Волков С.Д. Статистическая теория прочности. – М.-Свердловск: Машгиз, 1960. 176 с.