TECHNOLOGICAL PROPERTIES OF NANODISPERSIONS BASED ON DER-330 EPOXY RESIN AND BS-50 FUMED SILICA

The influence of silica dioxide nanoparticles in the form of fumed silica BS-50 on the rheological properties, residual shrinkage and shrinkage stresses upon curing an epoxy resin is considered. It is shown that the introduction of BS-50 in the optimum concentration of nanoparticles into DER-330 epoxy resin results in agglomeration, which is accompanied by an abnormal behavior of the disperse system with a decrease in viscosity by ~ 25%, ultimate shrinkage by ~ 15% and the level of residual stresses by a factor of ~ 4-10. These properties are manifested when the concentration of fumed silica is 0.05 vol. % The introduction of fumed silica slows the rise of residual stresses and increases the induction period from 2 to 4 hours. Depending on the mode of curing the minimum residual stress is observed at different concentrations of BS-50. At temperatures of 30ºC and 50°C concentration was 0.5 vol. %, and at 70°C - 0.05 vol. %. Curing at 30°C and 50°C result in a fall of residual stress by a factor of 12 and 4, respectively, at 70°C, by a factor of 4.

epoxy resin, nanoparticles, fumed silica, nanocomposite

1. The world of materials and technologies. Polymer nanocomposites / Ed. Wing May Yu, Zhong-Zhen Yu. M: Technosphere, 2011. 688 p. (in Russ.)

2. Ajayan P.M., Schadler L.S., Braun P.V. Nanocomposite Science and Technology. Weinheim, Germany: Wiley-VCH, 2003. 230 p.

3. Yudovich V.M., Morozov S.E., Yudovich M.E., Toikka A.M., Ponomarev A.N. // Vestnik of St. Petersburg State University. 2010. Ser. 4. V. 3. P. 36–44. (in Russ.)

4. Kartaman N.T., Azizov A.G., Osipchik V.S., Mammadli U.M., Arzumanova N.B. // Plasticheskie massy (Plastjournal). 2016. № 1-2. P. 49–57. (in Russ.)

5. Badamshina E.R., Gafurov M.P., Estrin J.I. // Uspekhi khimii (Russian Chemical Reviews). 2010. V. 79 (11). P. 1027–1064. (in Russ.)

6. Kablov E.N., Kondrashov S.V., Jurkov G.Y. // Russian Nanotechnologies. 2013. V. 8. № 3-4. Р. 28–46. (in Russ.)

7. Klenin V.I, Shchegolev S.Y., lavrushin V.I. Characteristic functions of light scattering disperse systems. Saratov: Publishing House of Saratov University, 1977. 177 p. (in Russ.)

8. Shchukin E.D., Colloidal chemistry: textbook for universities and chemical-technological universities / Shchukin E.D. [et al.]. M.: Khimiya, 2004. 445 p. (in Russ.)

9. Apeksimov N.V., Trofimov A.N., SimonovEmelyanov I.D. // Plasticheskie massy (Plastjournal). 2013. № 10. P. 13– 19. (in Russ.)

10. Sanzharov A.T. Methods for determining the mechanical and adhesion properties of polymer coatings. M.: Nauka, 1974. 274 p. (in Russ.)

11. Kudryashov S.Y., Onuchak L.A. Colloid chemistry: Laboratory workshop. Samara: Ed. «Universgroups», 2006. 48 р. (in Russ.)

12. Trostyansky E.B., Golovkin G.S. // Plasticheskie massy (Plastjournal). 1976. № 11. P. 11–17. (in Russ.)

13. Simonov-Emelyanov I.D., Kuleznev V.N. Principles of creation of composite materials. M.: MITHT, 1987. 76 р. (in Russ.)

14. Tanaka H., Araki T. // Chem. Eng. Sci. 2006. V. 61. P. 2108–2141.

15. Kuleznev V.N. Mixtures of the polymers. M.: Khimiya, 1978. 216 p. (in Russ.)

16. Kulichikhin V.G., Semakov A.V., Karbushev V.V., Plate N.A., Picken S.J. // Vysokomolekulyarnye soedineniya (Macromolecular compounds). 2009. V. 51. № 11. P. 2044–2053. (in Russ.)

17. Simonov-Emelyanov I.D., Apeksimov N.V., Trofimov A.N., Surikov P.V., Homjakov A.K. // Vestnik MITHT. 2011. V. 6. № 4. P. 89–92. (in Russ.)

18. Simonov-Emelyanov I.D., Surikov P.V., Trofimov A.N., Kandyrin L.B., Zarubin A.J., Apeksimov N.V. // Klei. Hermetiki. Tekhnologii (Adhesives. Sealants. Technology). 2012. № 12. P. 6–10. (in Russ.)