кандидат технических наук, доцент кафедры химии и технологии переработки пластмасс и полимерных композитов
119571, Россия, Москва, пр-т Вернадского, д. 86
Ph.D. (Engineering), Associate Professor of the Chair of Chemistry and Technology of Plastic Processing and Polymer Composites,
86, Vernadskogo pr., Moscow, 119571, Russia
кандидат технических наук, старший научный сотрудник кафедры химии и технологии переработки пластмасс и полимерных композитов
119571, Россия, Москва, пр-т Вернадского, д. 86
Ph.D. (Engineering), Senior Researcher of the Chair of Chemistry and Technology of Plastic Processing and Polymer Composites
86, Vernadskogo pr., Moscow, 119571, Russia
ассистент кафедры химии и технологии переработки пластмасс и полимерных композитов
119571, Россия, Москва, пр-т Вернадского, д. 86
Assistant of the Chair of Chemistry and Technology of Plastic Processing and Polymer Composites
86, Vernadskogo pr., Moscow, 119571, Russia
кандидат технических наук, старший научный сотрудник кафедры химии и технологии элементоорганических соединений имени К.А. Андрианова
119571, Россия, Москва, пр-т Вернадского, д. 86
Ph.D. (Engineering), Senior Researcher of the K.A. Andrianov Chair of Chemistry and Technology of Organoelement Compounds
86, Vernadskogo Pr., Moscow, 119571, Russia
кандидат технических наук, заведующая лабораторией кафедры химии и технологии переработки пластмасс и полимерных композитов
119571, Россия, Москва, пр-т Вернадского, д. 86
Ph.D. (Engineering), Head of the Laboratory of the Chair of Chemistry and Technology of Plastic Processing and Polymer Composites
86, Vernadskogo Pr., Moscow, 119571, Russia
доктор технических наук, профессор, заведующий кафедрой химии и технологии переработки пластмасс и полимерных композитов
119571, Россия, Москва, пр-т Вернадского, д. 86
D.Sc. (Engineering), Professor, Head of the Chair of Chemistry and Technology of Plastic Processing and Polymer Composites
86, Vernadskogo Pr., Moscow, 119571, Russia
By the method of capillary viscosimetry, the melt flow curves of the molded phenolic resin and its compositions with lubricant, plasticizer and their mixture were obtained. It was shown that the size (diameter) of the capillary channel influences the dependence of the effective shear rate on the shear stress (flow curves) of the studied compositions. Such rheological behavior of the compositions during flow is associated with the effect of sliding along the surface of the capillary wall. According to the Mooney method, the dependences of the effective shear rate at given values of shear stress on the reciprocal of the capillary radius are plotted. The function of the slip velocity on the shear stress on the capillary wall is characterized in terms of the slip coefficient, which relates the shear stress on the capillary wall to the velocity of the composition along it. For the studied compositions, the total flow through the capillary was divided into volume fractions, one of which is associated with a shear flow; the other is determined by the slip effect. It has been shown that the introduction of both a lubricant and a plasticizer into the composition leads to an increase in the fluidity of the compositions. At the same time, adding of lubricant increases the volume fraction of the slip flow. The greatest effect of increasing the fluidity of the composition gives the use of complex modifying additives containing both lubricant and plasticizer.
Методом капиллярной вискозиметрии получены кривые течения расплава литьевого фенопласта и его композиций со смазкой, пластификатором и их смесью. Показано, что на зависимости эффективной скорости сдвига от напряжения сдвига (кривые течения) исследованных композиций оказывает влияние размер (диаметр) канала капилляра. Подобное реологическое поведение композиций при течении связано с эффектом скольжения по поверхности стенки капилляра. По методу Муни построены зависимости эффективной скорости сдвига при заданных значениях напряжения сдвига от обратной величины радиуса капилляра. Функция скорости скольжения от напряжения сдвига на стенке капилляра охарактеризована через величину коэффициента скольжения, связывающего напряжение сдвига на стенке канала капилляра со скоростью скольжения по ней композиции. Для исследованных композиций проведено разделение общего потока через капилляр на объемные доли, одна из которых связана со сдвиговым течением, другая определяется эффектом скольжения. Показано, что введение в композицию как смазки, так и пластификатора приводит к повышению текучести композиций. При этом введение смазки увеличивает объемную долю потока скольжения. Наибольший эффект повышения текучести композиции дает применение комплексной модифицирующей добавки, содержащей и смазку, и пластификатор.